Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation
07:44

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation

Published on: March 15, 2017

[Study on the compositions in the interface of corrosion inhibition membrane/copper plating layer/iron substrate by

Shao-bin Feng1, Shi-bo Shang, Li-ting Feng

  • 1Zhengzhou Institute of Light Industry, Zhengzhou 450002, China.

Guang Pu Xue Yu Guang Pu Fen Xi = Guang Pu
|July 11, 2006
PubMed

More Related Videos

Accumulation and Analysis of Cuprous Ions in a Copper Sulfate Plating Solution07:00

Accumulation and Analysis of Cuprous Ions in a Copper Sulfate Plating Solution

Published on: March 20, 2019

Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media10:05

Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media

Published on: November 3, 2018

Related Concept Videos

Electrodeposition01:08

Electrodeposition

Electrodeposition is a technique used to separate an analyte from interferents by electrochemical processes. Here, the analyte is a metal ion that can be deposited on an electrode immersed in the sample solution. The electrochemical setup consists of an anode and a cathode. When an electric current is applied to the setup, oxidation occurs at the anode. At the cathode, which consists of a large metal surface, metal ions undergo reduction and deposit onto the surface.
Electrodeposition can...
Interfacial Electrochemical Methods: Overview01:06

Interfacial Electrochemical Methods: Overview

Interfacial electrochemical methods focus on the phenomena occurring at the boundary between an electrode and a solution, as opposed to bulk methods that concentrate on the solution's overall properties. These interfacial methods are classified as either static or dynamic based on the presence of a nonzero current in the electrochemical cell and the consistency of analyte concentrations. Static methods, such as potentiometry, measure the cell's potential without any significant current passing...
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
Precipitation and Co-precipitation01:17

Precipitation and Co-precipitation

Precipitation and coprecipitation methods can be used to separate a mixture of ions in a solution. In qualitative inorganic analysis, ions that form sparingly soluble precipitates with the same reagent are separated based on the differences in solubility products. For example, consider the separation of Cu(II) and Fe(II) ions by precipitation as insoluble sulfides. First, copper(II) sulfide is precipitated by the addition of acidic H2S, where the dissociation of H2S is suppressed. Adding H2S...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Extraction: Advanced Methods00:56

Extraction: Advanced Methods

Metal ions can be separated from one another by complexation with organic ligands–the chelating agent– to form uncharged chelates. Here, the chelating agent must contain hydrophobic groups and behave as a weak acid, losing a proton to bind with the metal. Since most organic ligands used in this process are insoluble or undergo oxidation in the aqueous phase, the chelating agent is initially added to the organic phase and extracted into the aqueous phase. The metal-ligand complex is formed in...