TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method
Published on: April 26, 2017
The formation of mesoporous TiO2 spheres via a facile chemical process
Yunxia Zhang1, Guanghai Li, Yucheng Wu
1Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031, People's Republic of China. zyxqm@yahoo.com.cn
Abstract:
The mesoporous TiO(2) solid and hollow spheres have been synthesized via a controllable and simple chemical route. Structural characterization indicates that these TiO(2) mesoporous spheres after calcined at 500 degrees C have an obvious mesoporous structure with the diameters of 200-300 nm for solid spheres and 200-500 nm for hollow spheres. The average pore sizes and BET surface areas of the mesoporous TiO(2) solid and hollow spheres are 6.8, 7.0 nm and 162, 90 m(2)/g, respectively. Optical adsorption investigation shows that TiO(2) solid and hollow spheres possess a direct band gap structure with the optical band gap of 3.68 and 3.75 eV, respectively. A possible formation mechanism for TiO(2) solid and hollow spheres is discussed.
More Related Videos
08:00Chemical Synthesis of Porous Barium Titanate Thin Film and Thermal Stabilization of Ferroelectric Phase by Porosity-Induced Strain
Published on: March 27, 2018
09:09A Facile Synthetic Method to Obtain Bismuth Oxyiodide Microspheres Highly Functional for the Photocatalytic Processes of Water Depuration
Published on: March 29, 2019