Nanostructured PtRu/C as anode catalysts prepared in a pseudomicroemulsion with ionic surfactant for direct methanol...

Nanostructured PtRu/C catalysts have been prepared from a water-in-oil pseudomicroemulsion with the aqueous phase of a mixed concentrated solution of H(2)PtCl(6), RuCl(3), and carbon powder, oil phase of cyclohexane, ionic surfactant of sodium dodecylbenzene sulfonate (C(18)H(29)NaO(3)S), and cosurfactant n-butanol (C(4)H(10)O). Two different composing PtRu/C nanocatalysts (catalyst 1, Pt 20 wt %, Ru 15 wt %; catalyst 2, Pt 20 wt %, Ru 10 wt %) were synthesized. The catalysts were characterized by transmission electron microscopy, X-ray diffractometry, X-ray photoelectron spectroscopy, and thermogravimetric analysis, and the particles were found to be nanosized (2-4 nm) and inherit the Pt face-centered cubic structure with Pt and Ru mainly in the zero valance oxidation state. The ruthenium oxide and hydrous ruthenium oxide (RuO(x)()H(y)()) were also found in these catalysts. The cyclic voltammograms (CVs) and chronoamperometries for methanol oxidation on these catalysts showed that catalyst 1 with a higher Ru content (15 wt %) has a higher and more durable electrocatalytic activity to methanol oxidation than catalyst 2 with low Ru content (10 wt %). The CV results for catalysts 1 and 2 strongly support the bifunctional mechanism of PtRu/C catalysts for methanol oxidation. The data from direct methanol single cells using these two PtRu/C as anode catalysts show the cell with catalyst 1 has higher open circuit voltage (OCV = 0.75 V) and maximal power density (78 mW/cm(2)) than that with catalyst 2 (OCV = 0.70 V, P(max) = 56 mW/cm(2)) at 80 degrees C.