Hydrogen storage capacity characterization of carbon nanotubes by a microgravimetrical approach

An accurate gravimetric apparatus based on a contactless magnetic suspension microbalance was developed. This unit was used to measure the hydrogen storage capacity for a variety of carbon nanotubes (CNTs) at room temperature and hydrogen pressures up to 11.5 MPa. The results show that regardless of their synthesis methods, purities, and nanostructures all investigated CNT products possess relatively low hydrogen storage capacities (<0.2 wt %). For comparison, the adsorption characteristics of theses samples were also measured at a pressure of 0.1 MPa and liquid nitrogen temperature (approximately 77 K) by a conventional volumetric approach. The methodological aspects related to the accuracy of the hydrogen uptake measurements are also discussed.