Augmentation of tendon attachment to porous ceramics by bone marrow stromal cells in a rabbit model

Tendon attachment to interconnected porous calcium hydroxyapatite ceramics (IP-CHA) with cultured bone marrow stromal cells (BMSC) was analysed. The purpose of this study was to evaluate whether BMSC in IP-CHA could augment the tendon attachment to IP-CHA histologically and biomechanically. Eighteen Japanese white rabbits were used. Cultured BMSCs were subcultured in IP-CHA. The grafted tendon and IP-CHA with BMSC complex were implanted in a bone defect of the knee [BMSC(+) group]. In the contralateral knee, a tendon and IP-CHA without BMSC complex were implanted [BMSC(-) group]. Histological findings of the interface between the tendon and IP-CHA were similar in the two groups 3 weeks after the operation. However, 6 weeks after the operation, more abundant bone formation around the tendon was observed in the BMSC(+) group. The direct apposition of the tendon to bone in pores and collagen fibre continuity between the tendon and fibrous tissue in pores were observed. In biomechanical evaluation, the maximum pull-out load of the tendon from the IP-CHA in the BMSC(+) group was significantly higher than that in the BMSC(-) group 6 weeks after the operation. BMSCs cultured in IP-CHA could augment tendon attachment to IP-CHA.