Photocatalytic degradation of C.I. Acid Red 27 by immobilized ZnO on glass plates in continuous-mode

The photocatalytic degradation of C.I. Acid Red 27 (AR27), an anionic monoazo dye of acid class, in aqueous solutions was investigated with immobilized ZnO catalyst on glass plates in a continuous-mode. In the slurry ZnO system the separation and recycling of the photocatalyst is practically difficult. Thus, ZnO was immobilized on solid supports to solve this problem. The removal percent increases with increasing the photoreactor volume and light intensity but it decreases when the flow rate is increased. With decreasing flow rate from 43 to 15mlmin(-1), the complete decolorization and degradation was obtained at around 748 and 1080cm(3) from photoreactor volume. The increase in the light intensity from 21.4 to 58.5Wm(-2) increases the decolorization from 23 to 57.6% and degradation from 17.5 to 37.8% for 374cm(3) of photoreactor volume. NH(4)(+), NO(3)(-), NO(2)(-) and SO(4)(2-) ions were analyzed as mineralization products of nitrogen and sulfur heteroatoms. Results showed that final concentration of SO(4)(2-) ions and N-containing mineralization products were less than the finally expected stoichiometric values. The positive slope of production of NH(4)(+), NO(3)(-) and NO(2)(-) shows that these compounds are initial products resulting directly from the initial attack on the nitrogen-to-nitrogen double bond (-NN-) of the azo dye.