Direct catalytic route to superhydrophobic polyethylene films
1Schuit Institute of Catalysis and Laboratory of Materials and Interface Chemistry, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands.
Abstract:
Polyethylene films grow on a flat silica surface modified by the bis(imino)pyridyl iron(II) catalyst during ethylene polymerization in toluene solvent. The resulting films show superhydrophobic properties. Advancing water contact angle as high as 169 degrees and sliding angles as low as 2 degrees are obtained on these films. SEM images reveal special surface structures of these films containing micrometer-sized islands, submicrometer particles on the islands, and stress nanofibers between the islands, which render superhydrophobicity to the polyethylene surfaces. After the submicrometer particles and stress nanofibers are removed by annealing, the superhydrophobic properties of the polymer films disappear.
Related Concept Videos
02:35Free-Radical Chain Reaction and Polymerization of Alkenes
01:20Types of Step-Growth Polymers: Polyesters
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the polymer...
00:53Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)
Similar to cross-metathesis, ADMET also involves the formation of metallacyclobutane intermediate by [2+2] cycloaddition of one of the double bonds of a terminal diene with...