Shear bond strength of glass-ionomer cements to air-abraded dentin
Wanessa Christine de Souza-Zaroni1, Vanessa Tessari Nhani, Juliane Cristina Ciccone-Nogueira
1Department of Restorative Dentistry, Ribeirio Preto School of Dentistry, University of São Paulo, Ribeirão Preto, SP, Brazil.
Purpose:
The aim of this in vitro study was to evaluate the shear bond strength of two conventional glass-ionomer cements to bovine dentin when using the air-abrasion technique for cavity preparation.
Materials And Methods:
Forty bovine central incisors were selected, embedded in polyester resin, and ground until the dentin surface was exposed. The teeth were randomly assigned to four groups: I and II--rotating instrument with a carbide bur; III and IV--an air-abrasion system. Groups I and III were restored with Fuji IX and groups II and IV with Ketac Molar. A 3-mm-diameter bonding site was delimited and treated with 10% polyacrylic acid for 10 s in the Fuji IX subgroups and with 25% polyacrylic acid for 10 s in the Ketac Molar subgroups. After surface treatment, a glassionomer cylinder was prepared for each specimen, using a split bisected Teflon matrix. The finished specimens were submitted to the shear bond strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The data were analyzed using ANOVA and Scheffé statistical tests. The dentin bonding areas were analyzed under a stereoscopic optical magnifier (40X) to assess the type of failure.
Results:
The mean (SD) shear bond strengths in MPa were: group I--3.49 (+/- 3.77), group II--7.17 (+/- 2.93), group III--7.55 (+/- 2.99), group IV--5.67 (+/- 3.90). Ketac Molar showed higher bond strength values in bur-prepared cavities, while on the air-abraded preparations, Fuji IX showed superior results.
Conclusion:
It can be concluded that the air-abrasion system used for cavity preparations may influence the bonding performance of conventional glass-ionomer cements to dentin.
Related Concept Videos
01:12Bonding and Strength of Aggregate
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons from...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
01:17Mortar Properties