Thirty-five percent carbamide peroxide application causes in vitro demineralization of enamel
Neslihan Efeoglu1, David J Wood, Candan Efeoglu
1Department of Fixed & Removable Prosthodontics, Level 6 Worsley Building, Leeds Dental Institute, University of Leeds, Clarendon Way, Leeds LS2 9LU, UK. n.efeoglu@leeds.ac.uk
Objectives:
The objective of this in vitro study was to investigate whether a high concentration 'in-office' bleaching agent affected the mineral content of enamel and dentin.
Methods:
A commercially available 35% carbamide peroxide bleaching agent was applied for 2h to sectioned teeth (n=11). Specimens were then immersed in artificial saliva at 37 degrees C for a further 24h to simulate the oral environment. Tomographic images of these sections were obtained (micro-CT 80, Scanco, Switzerland) prior to and post-bleach application. Eight three-dimensional regions of interest (ROI), starting from the enamel surface extending to the dentinoenamel junction, were selected for each section. The hydroxyapatite equivalent mineral concentrations (g/cm(3)) of the ROIs were calculated. Any changes in mineral content as a consequence of the bleaching procedure were calculated in relation to each ROI.
Results:
There was a significant reduction in the mineral content of enamel specimens post-bleach application extending to a depth of 250microm (paired t-test, p<0.05); this reduction in mineral content was greatest in the ROI's closest to the tooth surface. There was, however, no significant difference in the mineral content of dentin as a consequence of bleaching.
Significance:
This in vitro study has shown that significant demineralization of enamel occurred following bleaching with 35% carbamide peroxide. The concept that 'in-office' bleaching is a non-destructive cosmetic procedure should be reconsidered.