Determining biodegradability of plastic materials under controlled and natural composting environments

With the advent of recently promulgated Government regulations on plastics in Mauritius, a study was initiated to examine the biodegradability of two different types of plastic, namely Willow Ridge Plastics - PDQ-H additive (Plastic A) and Ecosafe Plastic - TDPA additive (Plastic B) under controlled and natural composting environments. The results obtained from the controlled composting environment showed that the cumulative carbon dioxide evolution for Plastic A was much higher than that for Plastic B. Plastic A therefore showed a higher level of biodegradation in terms of CO2 evolution than Plastic B. However, from the regression analysis, it was found that the level of CO2 varying with time fitted the sigmoid type curves with very high correlation coefficients (R2 values: 0.9928, 0.9921 and 0.9816, for reference material, inoculum and Plastic A, respectively). The corresponding F-values obtained from the ANOVA analysis together with significance levels of p<0.05 indicated that the three treatments analysed in the biodegradability experiment were significant. The other experiment was undertaken to observe any physical change of Plastics A and B as compared to a reference plastic, namely, compostable plastic bag (Mater-Bi product-Plastic C), when exposed to a natural composting environment. Thermophilic temperatures were obtained for about 3-5 days of composting and the moisture content was in the range of 60-80% throughout the degradation process. It was observed that after 55 days of composting, Plastic C degraded completely while Plastic A and Plastic B did not undergo any significant degradation. It can be concluded that naturally based plastic made of starch would degrade completely in a time frame of 60 days, whereas plastics with biodegradable additive would require a longer time.