Characterization of a novel calcium phosphate composite bone cement: flow, setting, and aging properties

M L Roemhildt1, S D Wagner, T D McGee

  • 1Department of Orthopaedics and Rehabilitation, University of Vermont, 95 Carrigan Drive, Burlington, VT 05403, USA. maria.roemhildt@med.uvm.edu

Journal of Materials Science. Materials in Medicine
|November 24, 2006
PubMed

More Related Videos

Comprehensive Characterization of Tissue Mineralization in an Ex Vivo Model07:29

Comprehensive Characterization of Tissue Mineralization in an Ex Vivo Model

Published on: September 27, 2024

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage11:51

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage

Published on: February 10, 2014

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...
Setting Time of Cement01:12

Setting Time of Cement

The setting time of cement refers to the process of cement paste transitioning from a plastic state to a solid state. This process is crucial in construction as it dictates the timeframe for concrete placement, compaction, and finishing. The onset of this solidification is termed the initial set, indicating when the paste becomes unworkable. The final set is when the paste has solidified completely, and further handling or manipulation can no longer affect its shape. The cement strength is...
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
Bone Remodeling01:40

Bone Remodeling

Bone remodeling is a continuous and balanced process of bone resorption by osteoclasts and bone formation by osteoblasts. In adults, it helps maintain bone mass and calcium homeostasis. While mechanical stress can stimulate turnover as part of the normal maintenance and reparative process, several hormones also regulate bone remodeling.
The Bone Matrix01:18

The Bone Matrix

Bone contains a relatively small number of cells entrenched in a matrix of collagen fibers that provide an adherent surface for inorganic salt crystals. Both components of the matrix, organic and inorganic, contribute to the unusual properties of bone. Without collagen, bones would be brittle and shatter easily. Without mineral crystals, bones would flex and provide little support. This can be observed by an experiment: when the minerals of a bone are dissolved by soaking the bone in acid or...
Bone Disorders01:29

Bone Disorders

Aging and its effect on bone remodeling is the most common cause of bone disorders. In young and healthy people, bone deposition and resorption happen at an equal rate to maintain optimal bone health.
Bone deposition is also affected by the levels of sex hormones like estrogen and testosterone that promote osteoblast activity and bone matrix synthesis. When the level of these hormones decreases due to aging, it causes a reduction in bone deposition. As a result, bone resorption by osteoclasts...