Nanocomposite and nanoporous polyaniline conducting polymers exhibit enhanced catalysis of nitrite reduction

Nanostructured polyaniline (PANI) conducting polymer films were prepared on electrochemically pretreated glassy carbon electrodes, which were previously modified with multilayers of polystyrene (PS) nanoparticles with a diameter of 100 nm. PANI was electropolymerised and grown through the interstitial spaces between the PS nanoparticles, which formed a nanocomposite film of PANI and PS nanoparticles on the electrode surface. Furthermore, a nanoporous PANI film was fabricated through the removal of the PS nanoparticles by dissolution in toluene. As a result of their nanostructure, both of the PANI films (before and after removal of the PS nanoparticles) exhibited enhanced electrocatalytic behaviour towards the reduction of nitrite relative to bulk-PANI films; however, partial collapse or shrinkage may have occurred with the removal of the nanoparticles and could have resulted in a less enhanced response. Under optimised conditions, the nanocomposite-film-modified electrode exhibited a fast response time of 5 s and a linear range from 5.0 x 10(-7) to 1.4 x 10(-3) M for the detection of nitrite; the detection limit was 2.4 x 10(-7) M at a signal-to-noise ratio of 3.