Development of high magnetization Fe3O4/polystyrene/silica nanospheres via combined miniemulsion/emulsion
Hong Xu1, Longlan Cui, Naihu Tong
1National Key Laboratory of Nano/Micro Fabrication Technology, Research Institute for Micro/Nano Science and Technology, Shanghai Jiaotong University, Shanghai 200030, PR China.
Abstract:
Monodispersed, hydrophilic, superparamagnetic magnetic nanospheres with a high fraction of magnetite were synthesized by combining modified miniemulsion/emulsion polymerization and sol-gel technique for the first time. The surface of the nanospheres was coated by a silica layer with controlled thickness. Transmission electron microscopy experimental results showed well-proportioned, equal-sized, magnetite/polystyrene (Fe3O4/PS) nanospheres with a thin silica shell. Based on the TGA data, the fraction of magnetite in the Fe3O4/PS nanospheres core was estimated to be 80 wt %. Magnetization measurements indicated that the superparamagnetic nature of the nanospheres had high saturation magnetization of 40 emu/g at 300 K. The procedures of the novel synthesis are described in detail. Also discussed are the mechanisms of the novel combined miniemulsion/emulsion polymerization processes.