Transport behavior of n-alkane penetrants into castor oil based polyurethane-polyester nonwoven fabric composites

Castor oil based polyurethane (PU)-polyester nonwoven fabric composites were fabricated by impregnating the polyester nonwoven fabric in a composition containing castor oil and diisocyanate. Composites were fabricated with two different isocyanates such as toluene-2,4-diisocyanate (TDI) and hexamethylene diisocyanate (HMDI). Transport behavior of n-alkane penetrants (pentane, hexane and heptane) into both PUs and PU-polyester nonwoven fabric composites were studied. Sorption studies were carried out at different temperatures. From the sorption results, the diffusion (D) and permeation (P) coefficients of penetrants have been calculated. Significant increase in the diffusion and permeation coefficients was observed with increase in the temperature of sorption experiments. Drastical reduction in diffusion and permeation coefficients was noticed in the composites compared to neat PUs. Attempts were made to estimate the empirical parameters like n, which suggests the mode of transport and K is a constant depends on the structural characteristics of the composite in addition to its interaction with penetrants. The temperature dependence of the transport coefficients has been used to estimate the activation energy parameter for diffusion (E(D)) and permeation (E(P)) processes from Arrhenius plots. Furthermore, the sorption results have been interpreted in terms of the thermodynamic parameters such as enthalpy (DeltaH) and entropy (DeltaS).