In vitro microhardness of glass ionomer cements

R C Silva1, A C C Zuanon, R R Esberard

  • 1Department of Pediatric Dentistry and Orthodontic, Araraquara Dental School, University of São Paulo State, UNESP, São Paulo, Brazil.

Journal of Materials Science. Materials in Medicine
|January 4, 2007
PubMed

Keywords:
dental material testingmicrohardness measurementrestorative dentistryin vitro dental studies

More Related Videos

Microhardness Measurements on Tooth and Alveolar Bone in Rodent Oral Disease Models06:16

Microhardness Measurements on Tooth and Alveolar Bone in Rodent Oral Disease Models

Published on: April 26, 2024

Related Concept Videos

Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in the...
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...