A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size
Published on: October 17, 2016
[Preparation of porous polylactic-acid/ bone matrix gelatin composite as scaffold materials for bone-tissue
Yu-min Zhang1, Bao-xing Li, Ji Li
1Research Center of Tissue Engineering, Southern Medical University, Guangzhou 510515, China. zymsir@sina.com
Objective:
To develop a novel porous poly lactic-acid(PLA)/bone matrix gelatin (BMG) bioactive composite biomaterial with supercritical carbon dioxide (SC-CO2) extraction and determine the optimal proportion of the ingredients by evaluating the physical and chemical characteristics and cellular compatibility of the composites.
Methods:
The PLA/BMG composite biomaterials with various PLA/BMG proportions were prepared with SC-CO2 technique and evaluated by macroscopic observation, porosity and mechanical assessment, and scanning electron micrograph (SEM). The optimal proportion of PLA/BMG was determined in conjunction with the results of cellular compatibility evaluation.
Results:
BMG proportion in BLA/BMG composite biomaterials prepared with SC-CO2 technique was positively associated with the cellular compatibility and porosity, and inversely with the mechanics of the prepared composite. The results showed BMG content of 30% in PLA/BMG composite was optimal.
Conclusion:
The composite with PLA and BMG proportion of 7:3 possesses good physical and chemical characteristics and cellular compatibility, suggesting its potential as the bone implant biomaterial and bone-tissue engineering scaffold.