Micropatterned biopolymer 3D scaffold for static and dynamic culture of human fibroblasts

During in vivo tissue regeneration, cell behavior is highly influenced by the surrounding environment. Thus, the choice of scaffold material and its microstructure is one of the fundamental steps for a successful in vitro culture. An efficacious method for scaffold fabrication should prove its versatility and the possibility of controlling micro- and nanostructure. In this paper, hyaluronic acid 3D scaffolds were developed through lamination of micropatterned membranes, fabricated after optimization of a soft-lithography method. The scaffold presented here is characterized by a homogeneous hexagonal lattice with porosity of 69%, specific surface area of 287 cm-1, and permeability of 18.9 microm2. The control over the geometry was achieved with an accuracy of 20 mum. This technique allowed not only fabrication of planar 3D scaffolds but also production of thin wall tubular constructs. Mechanical tests, performed on dry tubular scaffolds, show high rupture tensile strength. This construct could be promising not only as engineered vascular grafts but also for regeneration of skin, urethra, and intestinal walls. The biocompatibility of a 3D planar scaffold was tested by seeding human fibroblasts. The cells were cultured in both static and dynamic conditions, in a perfusion bioreactor at different flow rates. Microscope analysis and MTT test showed cell proliferation and viability and a uniform cell distribution likely due to an appropriate lattice structure.