Differential scanning calorimetry (DSC) and temperature-modulated DSC study of three mouthguard materials
Frank H Meng1, Scott R Schricker, William A Brantley
1Section of Orthodontics, College of Dentistry, The Ohio State University, Columbus, OH 43218, USA.
Objectives:
Employ differential scanning calorimetry (DSC) and temperature-modulated DSC (TMDSC) to investigate thermal transformations in three mouthguard materials and provide insight into their previously investigated energy absorption.
Methods:
Samples (13-21mg) were obtained from (a) conventional ethylene vinyl acetate (EVA), (b) Pro-form, another EVA polymer, and (c) PolyShok, an EVA polymer containing polyurethane. Conventional DSC (n=5) was first performed from -80 to 150 degrees C at a heating rate of 10 degrees C/min to determine the temperature range for structural transformations. Subsequently, TMDSC (n=5) was performed from -20 to 150 degrees C at a heating rate of 1 degrees C/min. Onset and peak temperatures were compared using ANOVA and the Tukey-Kramer HSD test. Other samples were coated with a gold-palladium film and examined with an SEM.
Results:
DSC and TMDSC curves were similar for both conventional EVA and Pro-form, showing two endothermic peaks suggestive of melting processes, with crystallization after the higher-temperature peak. Evidence for crystallization and the second endothermic peak were much less prominent for PolyShok, which had no peaks associated with the polyurethane constituent. The onset of the lower-temperature endothermic transformation is near body temperature. No glass transitions were observed in the materials. SEM examination revealed different surface morphology and possible cushioning effect for PolyShok, compared to Pro-form and EVA.
Significance:
The difference in thermal behavior for PolyShok is tentatively attributed to disruption of EVA crystal formation, which may contribute to its superior impact resistance. The lower-temperature endothermic peak suggests that impact testing of these materials should be performed at 37 degrees C.