Laser-diode-excited intense luminescence and green-upconversion in erbium-doped bismuth-germanate-lead glasses

We investigate the spectroscopic properties of the 1.5-microm emission from the (4)I(13/2)-->(4)I(15/2) transition of Er(3+) ions in bismuth-germanate-lead glasses for applications in broadband fiber amplifiers. The emission peak locates at 1532nm with a full width at half-maximum (FWHM) of approximately 65nm. The measured lifetime and the calculated emission cross-section of this transition are 3.3ms and 8.66x10(-21)cm(2), respectively. IR-to-green-upconversion occurs simultaneously upon excitation of the 1.5-microm emission with a commercially available 980nm laser diode. Effects of PbF(2) content on the thermal stability, structure and spectroscopic properties of Er(3+)-doped bismuth-germanate-lead glasses have been examined. We find that the substitution with PbF(2) provides a couple of potentials: shortening the UV cutoff band and decreasing the phonon energy of host glasses. Codoping of Yb(3+) significantly enhances both the green-upconversion and 1.5-microm emission intensity by means of a nonradiative Yb(3+)-->Er(3+) energy transfer. Energy transfer processes and nonradiative phonon-assisted decays could account for the population of the (2)H(11/2) level, which is an emitting level of the green-upconversion of Er(3+). The results indicate the possibility towards the development of bismuth-germanate-lead based glasses as photonics devices.