Shear bond strength of orthodontic brackets bonded using conventional vs one and two step self-etching/adhesive
Nuray Attar1, Tulin Ugur Taner, Erhan Tülümen
1Department of Conservative Dentistry, School of Dentistry, Hacettepe University, 06100, Shhiye, Ankara, Turkey. nurayattar@hotmail.com
Objective:
To assess and compare the effects of one- and two-step self-etching primer and adhesive with conventional acid-etching and bonding system on the shear bond strength of orthodontic brackets.
Materials And Methods:
The one-step self-etching primer and adhesive used was Clearfil tri-S bond, the two-step fluoride-releasing antibacterial self-etching primer and adhesive was Clearfil Protect Bond, and the fluoride-releasing conventional acid-etching and bonding system was Kurasper F Bond. Brackets were bonded to defect-free human premolars (n = 14 per group) according to each manufacturer's recommendations by using light-cured bracket adhesive Kurasper F Paste with a light-emitting diode of a light-curing unit. The specimens were stored in deionized water at 37 degrees C for 48 hours and then tested in shear with a universal testing machine at a crosshead speed of 5 mm/min until the brackets debonded. The mode of failure of the brackets was determined by a modified adhesive remnant index.
Results:
Mean shear bond strength values were 9.00 MPa for Kurasper F Bond, 9.55 MPa for Clearfil Protect Bond, and 9.48 MPa for Clearfil tri-S Bond. One-way analysis of variance detected no statistically significant difference among groups (P = .98, P > .05). The predominant failure for the three groups was at the bracket-adhesive interface leaving less than 25% of the adhesive on the bracket base.
Conclusions:
One-step self-etching adhesive and two-step fluoride-releasing antibacterial self-etching adhesive have sufficient mechanical properties for the bonding of orthodontic brackets.
Related Concept Videos
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons from...
01:12Bonding and Strength of Aggregate