Leaching of heavy metals from chromated copper arsenate (CCA) treated wood after disposal

Wood treated by preservatives is commonly found in solid waste. Among the different types of preserved wood, chromated copper arsenate (CCA) treated wood recently has received much attention due to the scale of usage and its significant role in soil and water contamination. As the ash of CCA treated wood would be hazardous if the wood were to be incinerated, this is not a good alternative, and the best available disposal method is thus landfilling in the US, Canada and Australia. Leaching of the metals from preserved wood that is disposed in unlined landfills for construction debris pollutes the soil and water environments. Several factors affecting leaching of the metals from wood, including pH of the leachant, temperature, the duration of leaching and the type of leachant, were investigated. These factors affect each of the metals, chromium, copper and arsenic, differently. A comparison of these effects on each metal was performed. The results of the experiments showed that the pH of the leachants has a significant effect on the leaching process, and sulfuric acid (pH 3) is the most effective leachant compared to nitric and acetic acid (pH 3-4-5). The amounts of leached chromium, copper and arsenic by sulfuric acid (pH 3) during 15 days were, respectively, 0.2, 0.14 and 0.15 mg more than leachates by nitric acid (pH 5) on the basis of 1g of wood (initial contents of 1.03 mg, 0.42 g and 0.8 mg per g of wood). Most of the leaching occurs in the first 5 days, and the rate of leaching decreases significantly after 5 days. Increasing temperature increases the amount of leached metals, and arsenic is the least resistant metal to the leaching when the temperature increases. Increasing the temperature from 15 degrees C to 35 degrees C during 15 days increases the amount of leached chromium, copper and arsenic by acetic acid at pH 5 by about 0.1, 0.4 and 1.2mg per g of wood, respectively.