Characterization of poly(ethylene imine) layers on mica by the streaming potential and particle deposition methods

Deposition kinetics of polystyrene latex (averaged particle size of 0.66 microm) on mica covered by poly(ethylene imine) (PEI), a cationic polyelectrolyte having an average molecular mass of 75,000 g mol(-1), was studied using the impinging-jet method. The hydrodynamic radius of PEI, determined by PCS measurements, was 5.3 nm. The electrophoretic mobility of PEI was measured as a function of pH for ionic strengths of 10(-3) and 10 (-2) M, which made it possible one to determine the amount of electrokinetic charge of the molecule and its zeta potential. Formation of the polyelectrolyte layer on mica was followed by measuring the streaming potential in the parallel-plate channel. From these measurements, the dependence of the apparent zeta potential of mica on the surface coverage of PEI was determined. The amount of adsorbed PEI on mica was calculated from the convective diffusion theory. These results were quantitatively interpreted in terms of the theoretical model postulating a particle-like adsorption mechanism for PEI with not too significant shape deformation upon adsorption. On the other hand, the Gouy-Chapman model postulating the adsorption in the form of flat disks was proved inappropriate. After the surface was fully characterized, particle deposition experiments were carried out with the aim of finding the correlation between the polymer coverage and the initial rate of latex particle deposition. In the range of small polyelectrolyte coverage, a monotonic relation between the polymer coverage and the initial deposition rate of particles, as well as the jamming coverage, was found. For Theta(PEI)>0.25, the initial particle deposition rate attained the value predicted from the convective diffusion theory for homogeneous surfaces. These results were interpreted theoretically by postulating that an effective immobilization of colloid particles occurred on local polyelectrolyte assemblages containing between two and three PEI molecules.