Unidirectional crystallization of charged colloidal silica due to the diffusion of a base

Dilute aqueous dispersions of charged colloidal silica (particle volume fraction = approximately 0.03-0.04, particle diameter = 110 nm) exhibit unidirectional crystal growth due to the diffusion of a weak base, pyridine (Py). Similar diffusion-crystallization is enabled by a salt of a weak acid and a strong base, sodium hydrogen carbonate (NaHCO3). The resulting crystals consist of columnar (or cubic) crystal grains with a maximum height of a few centimeters and a maximum width of 1 cm. The crystal growth process is attributed to a combination of (i) the diffusion of Py or NaHCO3 accompanied by a charging reaction of the silica particles and (ii) the charge-induced crystallization of the silica colloids. Theoretical growth curves based on the reaction-diffusion model for the case of Py were in good agreement with the observed curves. We also report the immobilization of the resulting large crystals by using a polymer hydrogel matrix.