UV surface modification of a new nanocomposite polymer to improve cytocompatibility

A novel modified nanocomposite was studied for the adhesion and proliferation of the human umbilical vein endothelial cell (HUVEC) line EA.hy926. The nanocomposite under investigation was poly(carbonate-urea)urethane with silsesquioxane nano-cages, here in the form of a mixture of two polyhedral oligomeric silsesquioxanes. The nanocomposite surfaces were exposed to ultraviolet (UV) light of a Xe(*)(2)-excimer lamp at a wavelength of 172 nm in an ammonia atmosphere. The effects of the irradiation were characterized by atomic force and scanning electron microscopy (AFM, SEM), X-ray photo-electron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FT-IR) using an attenuated total reflection (ATR) device and measurements of advancing water contact angle (CA). The irradiation resulted in the introduction of new hydrophilic N- and O-containing groups into the surface, which was initially amphiphilic, while surface morphology remained mainly unchanged. Slight chemical changes were also observed for the silsesquioxane nano-cages at the surface. Onto the untreated and irradiated samples HUVECs were seeded and grown for various durations in culture. Standard tissue-culture polystyrene (PS) was employed as a positive control to check the efficiency of the cell-culture methods. Viability and proliferation of the cells were then assessed using a non-radioactive assay. Compared to the untreated nanocomposite polymer, irradiation times of at least 5 min resulted in a significantly increased cell proliferation between 3 and 8 days after seeding with the HUVEC line EA.hy926.