Preparation and anticoagulation activity of sodium cellulose sulfate

Semi-synthesis of cellulose sulfate sodium (Na-MCS) was carried out by sulfation of microcrystalline cellulose (MCC) with chlorosulfonic acid-dimethylformamide complex as sulfating agent. As shown by FT-IR, NMR spectroscopy, and elemental analysis, the sulfation occurred mainly at C6, partially at C2, and no substitution at C3. The substitution degree ranged from 1.10 to 1.70 and the average molecular weight is between 1.1 and 3.5 x 10(4)Da. The anticoagulant efficacy and its possible mechanism were investigated using in vitro, in vivo coagulation assays and amidolytic tests in comparison with heparin. Results indicated that Na-MCS exhibited higher anticoagulation activity based on activated partial thromboplastin time (APTT) assay and prolonged the thrombin time (TT) to a lesser extent than heparin. No effect was detected on the prothrombin time (PT). Subcutaneous administration of Na-MCS to mice increased the clotting time (CT) in a moderate dose-dependent manner with a longer duration. Na-MCS exhibited anticoagulation activity mainly by accelerating the inhibition of antithrombin III (AT-III) on coagulation factors FIIa and FXa in plasma.