An Improved Mechanical Testing Method to Assess Bone-implant Anchorage
11:51

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage

Published on: February 10, 2014

Effect of weight-bearing on bone-bonding behavior of strontium-containing hydroxyapatite bone cement

G X Ni1, W W Lu, B Tang

  • 1Department of Rehabilitation Medicine, Fujian Medical University, Fuzhou, China [corrected]

Journal of Biomedical Materials Research. Part A
|July 4, 2007
PubMed

Keywords:
bone cement bondinghydroxyapatite cementweight-bearing effectsbone interface mechanics

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Essential Minerals for Bone Health01:31

Essential Minerals for Bone Health

The minerals contained in all of the food we consume are essential for our organ systems. However, certain essential minerals, such as calcium, phosphorus, magnesium, manganese, and fluoride, largely affect bone health.
Calcium and Phosphorus
Calcium is a critical component of bones, especially in the form of calcium phosphate and calcium carbonate. Since the body cannot make calcium, it must be obtained from the diet. However, calcium cannot be absorbed from the small intestine without...
The Bone Matrix01:18

The Bone Matrix

Bone contains a relatively small number of cells entrenched in a matrix of collagen fibers that provide an adherent surface for inorganic salt crystals. Both components of the matrix, organic and inorganic, contribute to the unusual properties of bone. Without collagen, bones would be brittle and shatter easily. Without mineral crystals, bones would flex and provide little support. This can be observed by an experiment: when the minerals of a bone are dissolved by soaking the bone in acid or...