Shape- and phase-controlled synthesis of monodisperse, single-crystalline ternary chalcogenide colloids through a...

Colloidal, monodisperse, single-crystalline pyramidal CuInS2 and rectangular AgInS2 nanocrystals were successfully synthesized through a convenient and improved solvothermal process that uses hexadecylamine as a capping reagent. The crystal phase, morphology, crystal lattice, and chemical composition of the as-prepared products were characterized by using X-ray diffraction, transmission electron microscopy (TEM), high-resolution TEM, and energy dispersive X-ray spectroscopy. Results revealed that the as-synthesized CuInS2 colloid is in the tetragonal phase (size: 13-17 nm) and the AgInS2 in the orthorhombic structure (size: 17+/-0.5 nm). A possible shape evolution and crystal growth mechanism has been suggested for the formation of pyramidal CuInS2 and rectangular AgInS2 colloids. Control experiments indicated that the morphology- and/or phase-change of CuInS2 and orthorhombic AgInS2 colloids are temperature- and/or time-dependent. CuInS2 colloids absorb well in the range of visible light at room-temperature, indicating its potential application as a solar absorber. Two photoluminescence (PL) subbands at 1.938 and 2.384 eV in the PL spectra of CuInS2 colloids revealed that the recombination of the closest and the second closest donor-acceptor pairs within the CuInS2 lattice, in which the donor defect (Cui) occupies an interstitial position and the acceptor defect (VIn) resides at an adjacent cation site. In addition, the synthesis strategy developed in this study is convenient and inexpensive, and could also be used as a general process for the synthesis of other pure or doped ternary chalcogenides that require a controlled size (or shape). This process could be extended to the synthesis of other functional nanomaterials.