Route to calculate the length scale for the glass transition in polymers

D Cangialosi1, A Alegría, J Colmenero

  • 1Donostia International Physics Center, Paseo Manuel de Lardizabal 4, 20018 San Sebastián, Spain. swxcacad@sw.ehu.es

Physical Review. E, Statistical, Nonlinear, and Soft Matter Physics
|August 7, 2007
PubMed

More Related Videos

Measuring the Mechanical Properties of Glass Fiber Reinforcement Polymer Composite Laminates Obtained by Different Fabrication Processes09:54

Measuring the Mechanical Properties of Glass Fiber Reinforcement Polymer Composite Laminates Obtained by Different Fabrication Processes

Published on: June 30, 2023

Synthesis of Programmable Main-chain Liquid-crystalline Elastomers Using a Two-stage Thiol-acrylate Reaction11:17

Synthesis of Programmable Main-chain Liquid-crystalline Elastomers Using a Two-stage Thiol-acrylate Reaction

Published on: January 19, 2016

Related Concept Videos

Determination of Molar Masses of Polymers II01:27

Determination of Molar Masses of Polymers II

Polymer samples typically consist of macromolecular chains with a distribution of lengths, resulting in a range of molar masses rather than a single discrete value. Conventional descriptors such as the number-average molar mass and weight-average molar mass quantify this distribution but do not fully capture polymer behavior in solution..The viscosity-average molar mass provides a more realistic description of polymer behavior in solution because it accounts for the enhanced contribution of...
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Determination of Molar Masses of Polymers I01:24

Determination of Molar Masses of Polymers I

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...
Classification and Mechanical Properties of Synthetic Polymers01:28

Classification and Mechanical Properties of Synthetic Polymers

Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.