Pre-overloading to extend fatigue life of cast clasps

A Mahmoud1

  • 1Department of Conservative Dentistry and Prosthodontics, Dental School, University of Jordan, Amman, Jordan. anabtawime@yahoo.com

Journal of Dental Research
|August 28, 2007
PubMed

More Related Videos

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting08:32

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting

Published on: May 14, 2016

Experimental Procedure for Warm Spinning of Cast Aluminum Components07:36

Experimental Procedure for Warm Spinning of Cast Aluminum Components

Published on: February 1, 2017

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
Residual Stresses01:26

Residual Stresses

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
Impact Loading01:19

Impact Loading

Impact loading occurs when a moving object collides with a stationary structure, such as a rod with a uniform cross-sectional area fixed at one end. Under these conditions, the rod absorbs the kinetic energy from the striking object, leading to deformation and subsequent stress development. As the rod returns to its original position and reaches maximum stress, the absorbed energy, initially manifested as kinetic energy, transforms entirely into strain energy.
In cases of elastic deformation,...
Machines: Problem Solving I01:22

Machines: Problem Solving I

A toggle clamp is a mechanical device commonly used for holding and clamping objects in various applications, such as woodworking, metalworking, and assembly operations. Consider a toggle clamp subjected to a force of 200 N at the handle. The vertical clamping force can be calculated, provided the dimensions of the toggle clamp are known.
The toggle clamp system is a machine structure consisting of movable, pin-connected multi-force members that form a stabilized system to transmit forces. The...
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and reloaded.