Assessment of polymerization contraction stress of three composite resins
Milena Cadenaro1, Matteo Biasotto, Nicola Scuor
1Department of Biomedicine, Division of Dentistry and Biomaterials, University of Trieste, Via Stuparich 1, I-34129 Trieste, Italy.
Objectives:
The purpose of this study was to measure the development of contraction stress of three composite resin restorative materials during photo-polymerization: a micro-hybrid composite (Filtek Z250, 3M ESPE, St. Paul, MN, USA); a nano-filled composite (Filtek Supreme, 3M ESPE, St. Paul, MN, USA); and a low-shrinkage composite (AElite LS, Bisco Inc., Schaumburg, IL, USA).
Methods:
Curing shrinkage stress was measured using a stress-analyzer. Composites were polymerized with a halogen-curing unit (VIP, Bisco Inc., Schaumburg, IL, USA) for 40 s. The contraction force (N) generated during polymerization was continuously recorded for 150 s after photo-initiation. Contraction stress (MPa) was calculated at 20, 40, 60 and 150 s. Data were statistically analyzed.
Results:
The low-shrinkage composite AElite LS exhibited the lowest stress values compared to other materials (p<0.05). Statistical analysis did not show significant differences between Filtek Z250 and Filtek Supreme.
Significance:
The low-shrinkage composite showed lower contraction stress than micro-hybrid and nano-filled composite. Ideally, non-shrinking resins would represent the ultimate solution to overcome polymerization contraction and stress-related problems.