Manganese oxide octahedral molecular sieves: preparation, characterization, and applications

A thermally stable 3 x 3 octahedral molecular sieve corresponding to natural todorokite (OMS-1) has been synthesized by autoclaving layer-structure manganese oxides, which are prepared by reactions of MnO(4)(-) and Mn(2+) under markedly alkaline conditions. The nature and thermal stability of products depend strongly on preparation parameters, such as the MnO(4)(-)/Mn(2+) ratio, pH, aging, and autoclave conditions. The purest and the most thermally stable todorokite is obtained at a ratio of 0.30 to 0.40. Autoclave treatments at about 150 degrees to 180 degrees C for more than 2 days yield OMS-1, which is as thermally stable (500 degrees C) as natural todorokite minerals. Adsorption data give a tunnel size of 6.9 angstroms and an increase of cyclohexane or carbon tetrachloride uptake with dehydration temperature up to 500 degrees C. At 600 degrees C, the tunnel structure collapses. Both Lewis and Brönsted acid sites have been observed in OMS-1. Particular applications of these materials include adsorption, electrochemical sensors, and oxidation catalysis.