Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Twenty-four hour flexural and shear bond strengths of flowable light-cured composites: a comparison analysis using

Rosalina Tjandrawinata1, Masao Irie, Kazuomi Suzuki

  • 1Department of Dental Materials, Faculty of Dentistry, Trisakti University, Campus B, JI. Kyai Tapa 260, Jakarta 11440, Indonesia.

Dental Materials Journal
|September 25, 2007
PubMed

More Related Videos

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates07:53

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates

Published on: April 27, 2019

Related Concept Videos

Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Bending of Members Made of Several Materials01:11

Bending of Members Made of Several Materials

In analyzing a structural member composed of two different materials with identical cross-sectional areas, it is crucial to understand how their distinct elastic properties affect the member's response under load. The analysis involves assessing stress and strain distributions using the transformed section concept, which accounts for variations in material properties.
Hooke's Law determines stress in each material, stating that stress is proportional to strain but varies due to each material's...
Relation Between Tensile Strength and Compressive Strength of Concrete01:30

Relation Between Tensile Strength and Compressive Strength of Concrete

Concrete is a fundamental building material, and understanding its strengths is crucial for construction projects. The relationship between its tensile and compressive strengths is intricate, showing that while these strengths are related, they do not increase at the same rate. Tensile strength's growth is slower and is affected by various factors such as the methods used for testing, the size and shape of the specimen, the texture of the aggregate used, and the moisture content of the concrete.
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...