Comparative study of silicone-hydrogel contact lenses surfaces before and after wear using atomic force microscopy
1Department of Physics (Optometry), School of Sciences, University of Minho, Portugal. mlira@fisica.uminho.pt
Purpose:
The aim of this study was to analyze surface changes of three silicone-hydrogel contact lenses after daily wear. The lenses used in this study were balafilcon A, lotrafilcon B (both surface-treated), and galyfilcon A (non surface-treated).
Methods:
To understand how and where proteins, lipids, and other contaminants change contact lenses, surface roughness was assessed through Atomic Force Microscopy Tapping Mode. Roughness parameters were Mean Surface roughness (R(a)), Mean-square-roughness (R(q)), and Maximum roughness (R(max)). The surface topography of unworn and worn lenses was also mapped in great detail.
Results:
Contact lenses roughness parameters exhibited different values before and after wear and the surface appearance also changed. After wear, balafilcon A and galyfilcon A showed a significant increase on surface roughness parameters, being this increase more accentuated to galyfilcon A. In lotrafilcon B materials no significant changes were observed with wear.
Conclusions:
The present study suggests that surface treatment of silicone-hydrogel contact lenses can play a role in the prevention of a significant increase in roughness, and contribute to the better clinical tolerance of these lenses.