Estimation of shelf life of natural rubber latex exam-gloves based on creep behavior

Samples of full-length glove-fingers cut from chlorinated and nonchlorinated latex medical examination gloves were aged for various times at several fixed temperatures and 25% relative humidity. Creep testing was performed using an applied stress of 50 kPa on rectangular specimens (10 mm x 8 mm) of aged and unaged glove fingers as an assessment of glove loosening during usage. Variations in creep curves obtained were compared to determine the threshold aging time when the amount of creep became larger than the initial value. These times were then used in various models to estimate shelf lives at lower temperatures. Several different methods of extrapolation were used for shelf-life estimation and comparison. Neither Q-factor nor Arrhenius activation energies, as calculated from 10 degrees C interval shift factors, were constant over the temperature range; in fact, both decreased at lower temperatures. Values of Q-factor and activation energies predicted up to 5 years of shelf life. Predictions are more sensitive to values of activation energy as the storage temperature departs from the experimental aging data. Averaging techniques for prediction of average activation energy predicted the longest shelf life as the curvature is reduced.