Evaluation of intragranular misorientation parameters measured by EBSD in a hot worked austenitic stainless steel

D Jorge-Badiola1, A Iza-Mendia, I Gutiérrez

  • 1CEIT and Tecnun (University of Navarra), P Manuel de Lardizabal, 15, 20018 Donostia-San Sebastián, Basque Country, Spain.

Journal of Microscopy
|November 30, 2007
PubMed

More Related Videos

Comprehensive Characterization of Extended Defects in Semiconductor Materials by a Scanning Electron Microscope11:14

Comprehensive Characterization of Extended Defects in Semiconductor Materials by a Scanning Electron Microscope

Published on: May 28, 2016

Optimized Setup and Protocol for Magnetic Domain Imaging with In Situ Hysteresis Measurement09:43

Optimized Setup and Protocol for Magnetic Domain Imaging with In Situ Hysteresis Measurement

Published on: November 7, 2017

Related Concept Videos

Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used to...
Temperature Dependent Deformation01:12

Temperature Dependent Deformation

In a nonhomogeneous rod made up of steel and brass, restrained at both ends and subjected to a temperature change, several steps are involved in calculating the stress and compressive load. Due to the problem's static indeterminacy, one end support is disconnected, allowing the rod to experience the temperature change freely. Next, an unknown force is applied at the free end, triggering deformations in the rod's steel and brass portions. These deformations are then calculated and added together...