H2 uptake and synthesis of the Li-dispersed manganese oxide nanotubes

Well aligned Li-dispersed manganese oxide nanotubes were prepared using LiNO3, Mn(NO3)2 x xH2O and an anodic aluminum oxide template by solvent-free method for potential applications in H2 storage. The obtained nanotubes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The analyses revealed the Mn2O3 nanotubes to have a cubic structure with a uniform length, 40-50 nm in wall thickness and 250 +/- 10 nm in the outer diameter. The level of H2 adsorption was determined using the gravimetric method. The Li-dispersed manganese oxide nanotubes showed a 0.26 wt% for the amount of hydrogen adsorption at 77 K under 4.5 MPa.