Study of a chemically amplified resist for X-ray lithography by Fourier transform infrared spectroscopy

Future applications of microelectromechanical systems (MEMS) require lithographic performance of very high aspect ratio. Chemically amplified resists (CARs) such as the negative tone commercial SU-8 provide critical advantages in sensitivity, resolution, and process efficiency in deep ultraviolet, electron-beam, and X-ray lithographies (XRLs), which result in a very high aspect ratio. In this investigation, an SU-8 resist was characterized and optimized for X-ray lithographic applications by studying the cross-linking process of the resist under different conditions of resist thickness and X-ray exposure dose. The exposure dose of soft X-ray (SXR) irradiation at the average weighted wavelength of 1.20 nm from a plasma focus device ranges from 100 to 1600 mJ/cm(2) on the resist surface. Resist thickness varies from 3.5 to 15 mum. The cross-linking process of the resist during post-exposure bake (PEB) was accurately monitored using Fourier transform infrared (FT-IR) spectroscopy. The infrared absorption peaks at 862, 914, 972, and 1128 cm(-1) in the spectrum of the SU-8 resist were found to be useful indicators for the completion of cross-linking in the resist. Results of the experiments showed that the cross-linking of SU-8 was optimized at the exposure dose of 800 mJ/cm(2) for resist thicknesses of 3.5, 9.5, and 15 microm. PEB temperature was set at 95 degrees C and time at 3 min. The resist thickness was measured using interference patterns in the FT-IR spectra of the resist. Test structures with an aspect ratio 3:1 on 10 microm thick SU-8 resist film were obtained using scanning electron microscopy (SEM).