Rheology of aqueous solutions of polyglycidol-based analogues to pluronic block copolymers

The aqueous solution properties of a series of polyglycidol-poly(propylene oxide)-polyglycidol (PG-PPO-PG) block copolymers were investigated by means of rheology. The copolymers are considered as analogues to the commercially available Pluronic, poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO), block copolymers in which the flanking PEO blocks are substituted by blocks of structurally similar PG bearing a hydroxyl group in each repeating monomer unit. In the dilute regime, the samples normally behave as Newtonian fluids. Shear thinning was observed only for the solutions of LGP65 (the copolymer of 50 wt % PG content) as well as at concentrations well above the critical micellization concentration for the rest of the copolymers. The zero shear viscosities exhibited pronounced maxima at PG content of 50 wt % and were found to decrease with increasing temperature. The concentrated solutions were investigated using oscillatory measurements. Large hystereses were observed during the temperature sweeps 15-70-15 degrees C. The evolutions of the loss and storage moduli with frequency, PG content, and temperature displayed transitions from a non-elastic to elastic behavior of the solutions. A phase diagram showing areas of predominant elasticity or fluidity was constructed.