Ultrasonically initiated emulsion polymerization of styrene in the presence of Fe2+

Ultrasonically initiated emulsion polymerization of styrene was carried out in the presence of Fe(2+). The addition of a small amount of Fe(2+) markedly enhanced the polymerization rate of styrene. In the presence of 50 microM Fe(2+), the conversion of monomer in the reaction time of 60 min was 2.4 times as high as that in the absence of Fe(2+). The increase in the polymerization rate was due to higher concentration of hydroxyl (*OH) radicals generated via Fenton reaction of Fe(2+) with hydrogen peroxide (H(2)O(2)), which was proved by a lower amount of H(2)O(2) in Fe(2+) aqueous solution compared with that in pure water during ultrasonic irradiation. However, the addition of excessive Fe(2+) had no further accelerating effect on the polymerization rate due to the reduction of *OH radicals by Fe(2+). So it is an effective way to add an appropriate amount of Fe(2+) to accelerate ultrasonically initiated emulsion polymerization of styrene.