The influence of one-step polishing systems on the surface roughness and microhardness of nanocomposites
Yonca Korkmaz1, Emre Ozel, Nuray Attar
1Department of Conservative Dentistry, School of Dentistry, Baskent University, Ankara, Turkey. yoncako@yahoo.com
Objectives:
This in vitro study evaluated the surface roughness and microhardness of nanocomposites that contain nanoparticles and a microhybrid composite finished and polished with two different one-step polishing systems and a conventional multi-step polishing system.
Methods And Materials:
The materials evaluated were Filtek Supreme XT, Grandio, Ceram X, Aelite Aesthetic Enamel, Tetric EvoCeram and Filtek Z250. A total of 240 specimens (10-mm in diameter, 2 mm thick) were fabricated for both tests (n=120 each test) in a plexiglass mold covered with a Mylar strip. After polymerization, five specimens per group received no polishing treatment and served as the control for both tests. For each composite group (n=15), the specimens were randomly divided into three polishing systems: PoGo, OptraPol and Sof-Lex. All polishing systems were applied according to the manufacturers' instructions after being ground wet with 1200 grid silicon carbide paper. The surface roughness values were determined using a profilometer. The microhardness measurements were performed using a digital microhardness tester (load 500 g; dwell time 15 seconds). The data were analyzed using the one-way ANOVA test at a significance level of 0.05 for both tests. Multiple comparison was performed with the Duncan Multiple Range test.
Results:
The smoothest surfaces were achieved under Mylar strips in all composite groups (p<0.05). There were no statistically significant differences between polishing systems in the Filtek Supreme XT, Ceram X, Aelite Aesthetic Enamel and Grandio groups for surface roughness (p>0.05). In the Tetric EvoCeram group, Sof-Lex exhibited the highest roughness values. No statistically significant differences were evaluated between polishing systems (p>0.05); whereas, the surfaces under Mylar Strip showed statistically significant lower values than the polished surfaces in terms of microhardness (p<0.05).
Conclusion:
One-step polishing systems may be successfully used for polishing nanocomposites.