Size dependent magnetization and high-vacuum annealing enhanced ferromagnetism in Zn(1-x)Co(x)O nanowires
Wen-Bin Jian1, I-Jan Chen, Tai-Ching Liao
1Department of Electrophysics, National Chiao Tung University, Hsinchu 30010, Taiwan.
Abstract:
Diameter controllable ZnO nanowires have been fabricated by thermal evaporation (vapor transport) with various sizes of gold nanoparticles as catalysts. Diluted magnetic semiconductor (DMS) Zn(1-x)Co(x)O nanowires were then made by high energy Co ion implantation. The as-implanted and the argon-annealed Zn(1-x)Co(x)O nanowires displayed weak ferromagnetism while the high-vacuum annealed nanowires exhibited strong ferromagnetic ordering at room temperature. Size dependent behavior has been observed in the magnetic field and temperature dependences of magnetization. The shrinkage of the nanowire diameter reduced the spontaneous magnetization as well as the hysteresis loops. Field cooled and zero-field cooled magnetization and coercivity measurements were performed between 2 and 300 K to study the evolution of magnetism from the weak to the strong ferromagnetic states. In particular, superparamagnetic features were observed and shown to be intrinsic characteristics of the DMS Zn(1-x)Co(x)O nanowires. The room-temperature spontaneous magnetization of individual Zn(1-x)Co(x)O nanowires was also established by using magnetic force microscope measurements.
More Related Videos
09:06Visualizing Uniaxial-strain Manipulation of Antiferromagnetic Domains in Fe1+YTe Using a Spin-polarized Scanning Tunneling Microscope
Published on: March 24, 2019
08:55Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses
Published on: June 7, 2018
Related Concept Videos
01:31Ferromagnetism
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.