Recycling of harbor sediment as lightweight aggregate

Yu-Ling Wei1, Jing-Chiang Yang, Yong-Yang Lin

  • 1Department of Environmental Science and Engineering, Tunghai University, Taichung City 407 Taiwan. yulin@thu.edu.tw

Marine Pollution Bulletin
|May 13, 2008
PubMed

More Related Videos

Resource Recycling of Red Soil to Synthesize Fe2O3/FAU-type Zeolite Composite Material for Heavy Metal Removal05:52

Resource Recycling of Red Soil to Synthesize Fe2O3/FAU-type Zeolite Composite Material for Heavy Metal Removal

Published on: June 2, 2022

Field Collection and Laboratory Maintenance of Canopy-Forming Giant Kelp to Facilitate Restoration14:44

Field Collection and Laboratory Maintenance of Canopy-Forming Giant Kelp to Facilitate Restoration

Published on: June 7, 2024

Related Concept Videos

Deleterious Substances in Aggregate01:25

Deleterious Substances in Aggregate

Deleterious substances in aggregates can be detrimental to the quality and durability of concrete. These substances include organic impurities like loam, which interfere with cement hydration and are usually present in the sand. These prevent a good bond between aggregate and cement paste. Organic impurities can be detected using the colorimetric test, where the darkness of a solution after agitation indicates the level of organic content.
Another type of impurity is clay and fine material that...
Design Example: Aggregate Gradation01:24

Design Example: Aggregate Gradation

The right type and quality of aggregates are crucial for concrete as they significantly influence its properties, mix proportions, and cost-effectiveness. If different sources are available for sand, the commonly used fine aggregate in concrete, the selection of sand is primarily based on its gradation.
The grading, or particle-size distribution, of sand is determined using sieve analysis, with standard sizes ranging from 150 μm to 10 mm (ASTM No. 100 sieve to 3⁄8 in. sieve). Sand is sampled...
Aggregates Classification01:29

Aggregates Classification

Aggregate classification is generally based on its size, petrographic characteristics, weight, and source. Size classification ranges from coarse to fine aggregates, defined by the size of the particles. Coarse aggregates are particles that do not pass through ASTM sieve No. 4, and aggregates that pass through the sieve are fine aggregates.
Petrographic classification groups aggregates based on common mineralogical characteristics. Some of the common mineral groups found in aggregates are...
Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in the...
Preplaced Aggregate Concrete01:29

Preplaced Aggregate Concrete

Preplaced aggregate concrete is ideal for construction environments that are not easily accessible. The process begins by properly wetting the gap-graded coarse aggregates to remove the dirt, then placing it in the form and compacting it. Voids are filled with a mortar mix pumped under pressure through slotted pipes. This mortar typically consists of Portland cement, pozzolan, fine aggregates, water, and a fluidizing aid. The pozzolan helps reduce bleeding and segregation while improving the...
Additives and Fillers in Concrete01:29

Additives and Fillers in Concrete

Additives and fillers are integral to enhancing the properties of concrete. Pozzolans and blast-furnace slag are additives or admixtures due to their reactions with calcium hydroxide released during cement hydration. Fillers, which are finely ground and similar in fineness to Portland cement, improve concrete attributes such as workability density, and reduce capillary bleeding or cracking. Some fillers possess hydraulic properties or participate in benign reactions within the cement paste.
The...