[The expansion characters of a quick-heating gypsum-bonded investment under different heating methods]

Ming-Sheng Chen1, Xu Tong, Yu-Kun Meng

  • 1State Key Laboratory of Oral Diseases, Sichuan University, Chengdu 610041, China.

Hua Xi Kou Qiang Yi Xue Za Zhi = Huaxi Kouqiang Yixue Zazhi = West China Journal of Stomatology
|July 9, 2008
PubMed
Abstract

More Related Videos

Fused Filament Fabrication (FFF) of Metal-Ceramic Components08:43

Fused Filament Fabrication (FFF) of Metal-Ceramic Components

Published on: January 11, 2019

Metal-silicate Partitioning at High Pressure and Temperature: Experimental Methods and a Protocol to Suppress Highly Siderophile Element Inclusions11:50

Metal-silicate Partitioning at High Pressure and Temperature: Experimental Methods and a Protocol to Suppress Highly Siderophile Element Inclusions

Published on: June 13, 2015

Related Concept Videos

Thermal Expansion01:22

Thermal Expansion

The expansion of alcohol in a thermometer is one of many commonly encountered examples of thermal expansion, which is the change in size or volume of a given system as its temperature changes. The most visible example is the expansion of hot air. When air is heated, it expands and becomes less dense than the surrounding air, which then exerts an upward force on the hot air to, for example, make steam and smoke rise, and hot air balloons float. The same behavior happens in all liquids and gases,...
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
Expansion and Contraction in Masonry Walls01:19

Expansion and Contraction in Masonry Walls

Masonry walls are subject to slight expansion and contraction due to variations in temperature and moisture. Thermal movement in masonry is relatively straightforward to measure and plan for. On the other hand, moisture movement poses more of a challenge. New clay masonry units typically absorb water and expand over time under normal environmental conditions. Conversely, new concrete masonry units tend to shrink as they lose the excess moisture acquired during their production process.
To...
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
Accelerated Curing of Concrete01:25

Accelerated Curing of Concrete

Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.