Improving fracture toughness of dental nanocomposites by interface engineering and micromechanics

The fracture toughness of dental nanocomposites fabricated by various methods of mixing, silanization, and loadings of nanoparticles had been characterized using fatigue-precracked compact-tension specimens. The fracture mechanisms near the crack tip were characterized using atomic force microscopy (AFM), transmission electron microscopy (TEM), and scanning electron microscopy (SEM). The near-tip fracture processes in the nanocomposties were identified to involve several sequences of fracture events, including: (1) particle bridging, (2) debonding at the poles of particle/matrix interface, and (3) crack deflection around the particles. Analytical and finite-element methods were utilized to model the observed sequences of fracture events to identify the source of fracture toughness in the dental nanocomposites. Theoretical results indicated that silanization and nanoparticle loadings improved the fracture toughness of dental nanocomposites by a factor of 2 to 3 through a combination of enhanced interface toughness by silanization, crack deflection, as well as crack bridging. A further increase in the fracture toughness of the nanocomposites can be achieved by increasing the fracture toughness of the matrix, nano-filled particles, or the interface.