Micellar structures of poly(styrene-b-4-vinylpyridine)s in THF/toluene mixtures and their functionalization with gold
1Department of Polymer Science, Kyungpook National University, 1370 Sangyuk-dong, Buk-gu, Daegu 702-701, Korea.
Abstract:
The effects of the block copolymer composition and the solvent selectivity on the micellar morphologies of poly(styrene- b-4-vinylpyridine)s (PS- b-P4VPs) and their functionalizations with gold were studied in 10 mg/mL solutions using small-angle X-ray scattering and transmission electron microscopy (TEM). The solvent selectivity for the PS block was controlled by toluene/tetrahydrofuran (THF) mixtures in which toluene and THF are selective for PS and nonselective, respectively. The micellar structure was strongly dependent on phi (wt % toluene in toluene/THF mixture) and the composition of the block copolymers. PS(12K)- b-P4VP(11.8K) (symmetric) showed spherical micelles in the entire range of phi except phi = 0 (THF, nonselective solvent). PS(3.3K)- b-P4VP(18.7K) (asymmetric, longer P4VP) showed multiple morphologies with transitions from spheres to cylinders and finally to vesicles with an increase in phi. PS(19.6K)- b-P4VP(5.1K) (asymmetric, longer PS) showed spherical micelles only at the narrow ranges of 90 wt %
More Related Videos
09:02Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization
Published on: July 9, 2015
08:09A Technique to Functionalize and Self-assemble Macroscopic Nanoparticle-ligand Monolayer Films onto Template-free Substrates
Published on: May 9, 2014