[Characterization of homemade fast investment material for the IPS-Empress2 castable ceramic]

Gang He1, Yuankun Cen, Zuli Sheng

  • 1Hangzhou Hengha Dental Hospital, Hangzhou 310013, China.

Sheng Wu Yi Xue Gong Cheng Xue Za Zhi = Journal of Biomedical Engineering = Shengwu Yixue Gongchengxue Zazhi
|August 13, 2008
PubMed

Keywords:
dental investment materialceramic casting propertieshomemade dental materialsIPS-Empress2 ceramic

More Related Videos

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)08:29

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Published on: January 7, 2019

Fused Filament Fabrication (FFF) of Metal-Ceramic Components08:43

Fused Filament Fabrication (FFF) of Metal-Ceramic Components

Published on: January 11, 2019

Related Concept Videos

Bricks01:14

Bricks

Bricks, a fundamental building material, are crafted from fired clay and exhibit a range of shapes, sizes, and colors. The production process starts with extracting local clay or shale, which is then crushed, ground, and screened for a fine texture. The refined material is blended with water, creating a pliable mixture that can be formed into bricks using one of three processes: soft mud, dry press, or stiff mud methods.
Soft mud bricks are shaped in molds with high moisture content and can be...
Manufacture of Concrete Masonry Units01:27

Manufacture of Concrete Masonry Units

The process of manufacturing concrete masonry units begins by mixing stiff concrete composed of Portland cement, aggregates, and water. This mixture is then poured into metal molds. To ensure the concrete settles uniformly and to avoid separation of its components, the mixture in the molds is subjected to vibration. Shortly after, the still-wet blocks are removed from the molds and placed on racks.
These wet blocks are then transported for curing, which can occur in one of two environments: a...
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.