Wear of cross-linked polyethylene against itself: a material suitable for surface replacement of the finger joint

Cross-linking of polyethylene (XLPE) has dramatically improved its properties in industrial applications, and it may also have some application in the field of human joint replacement. Additionally it has the advantage of permitting a lower molecular weight base material to be used, so that components may be injection moulded rather than machined. This study therefore investigates the wear resistance of medical grade cross-linked polyethylene (XLPE), cross-linked by a silane-grafting process, with a molecular weight between cross links of 5430 g mol(-1). This first report investigates the wear resistance of XLPE against itself, because for certain joints, such as the metacarpo-phalangeal joint, the material may have a high enough wear resistance to allow both bearing surfaces to be made from it. Tests were carried out both on a reciprocating pin and plate machine with pins loaded at 10 and 40 N and also on a new finger joint simulator, which simulates the loads applied to and the movements of, the metacarpo-phalangeal joint. An average wear rate of 1.8 x 10(-6) mm3 N-1 m-1 was found (range 0.9-2.75 x 10(-6) mm3 N-1 m-1). This is about six times greater than the wear rate of non-cross-linked ultra high molecular weight polyethylene (UHMWPE) against stainless steel, but for applications with low loading, such as the metacarpo-phalangeal joint, this material is shown to have adequate wear resistance. The coefficient of friction was 0.1, which is similar to that of UHMWPE on stainless steel.