Inhibition of microbial concrete corrosion by Acidithiobacillus thiooxidans with functionalised zeolite-A coating

Tesfaalem Haile1, George Nakhla

  • 1Department of Civil and Environmental Engineering, University of Western Ontario, London, ON, Canada.

Biofouling
|October 11, 2008
PubMed

More Related Videos

Resource Recycling of Red Soil to Synthesize Fe2O3/FAU-type Zeolite Composite Material for Heavy Metal Removal05:52

Resource Recycling of Red Soil to Synthesize Fe2O3/FAU-type Zeolite Composite Material for Heavy Metal Removal

Published on: June 2, 2022

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight10:27

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight

Published on: October 11, 2016

Related Concept Videos

Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
Acid Attack on Concrete01:21

Acid Attack on Concrete

When acids come into contact with concrete, they initiate a chemical reaction that dissolves the hydrated cement paste. This process leads to softening and structural weakening of the concrete. This issue is commonly observed in environments such as chimneys, sewers, and industrial settings. The severity of the damage increases as the pH of the water interacting with the concrete drops below 6.5. In particular, a pH under 4.5 can cause significant concrete damage.
The rate at which hydrogen...
Waterproofing and Anti-Bacterial Admixtures in Concrete01:22

Waterproofing and Anti-Bacterial Admixtures in Concrete

Concrete's susceptibility to water absorption is due to the capillary action within the pores of its hydrated cement paste. This action draws water in, creating the need for waterproofing admixtures to prevent such penetration. The efficacy of these admixtures is contingent upon the water pressure, with variations arising from different conditions such as rain, capillary rise, or hydrostatic pressure in structures intended to hold water.
Waterproofing admixtures render concrete hydrophobic,...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Sulfate Attack on Concrete01:29

Sulfate Attack on Concrete

Sulfate attack on concrete is a deterioration process characterized by a whitish discoloration beginning at the edges and corners, accompanied by cracking and spalling. This phenomenon occurs when sulfates react with the components of hardened concrete, forming compounds like calcium sulfate and calcium sulfoaluminate which occupy more space than the substances they replace, causing the concrete to expand and disrupt.
Sulfates from sources like soil, groundwater, or industrial effluents...
Alkali Aggregate Reaction in Concrete01:26

Alkali Aggregate Reaction in Concrete

The alkali-aggregate reaction in concrete involves natural siliceous minerals in aggregates reacting with alkaline hydroxides derived from cement alkalis. This reaction forms an alkali-silica gel that absorbs water, swells, and increases in volume, which is confined by the surrounding cement paste, creating internal pressures that crack and disrupt the concrete. The extent of expansion and damage can be partly attributed to the alkali-silica reaction's osmotic hydraulic pressure and the...