Adhesion of sealer cements to dentin with and without the smear layer

The influence of a smear layer on the adhesion of sealer cements to dentin was assessed in recently extracted human anterior teeth. A total of 120 samples was tested, 40 per sealer; 20 each with and without the smear layer. The teeth were split longitudinally, and the internal surfaces were ground flat. One-half of each tooth was left with the smear layer intact, while the other half had the smear removed by washing for 3 min with 17% EDTA followed by 5.25% NaOCl. Evidence of the ability to remove the smear layer was verified by scanning electron microscopy. Using a specially designed jig, the sealer was placed into a 4-mm wide x 4-mm deep well which was then set onto the tooth at a 90-degree angle and allowed to set for 7 days in 100% humidity at 37 degrees C. This set-up was then placed into a mounting jig which was designed for the Instron Universal Testing Machine so that only a tensile load was applied without shearing or applying preloading forces. The set-up was subjected to a tensile load at a crosshead speed of 1 mm per min. The results show significant differences (p less than 0.001) among AH26, Sultan, and Sealapex, with AH26 being the strongest and Sealapex being the weakest. The only significant difference with regard to the presence or absence of the smear layer was found with AH26, which had a stronger bond when the smear layer was removed.