Determination of indium in high purity antimony by electrothermal atomic absorption spectrometry (ETAAS) using boric...

The use of boric acid as a modifier for the determination of trace amount of indium in high purity antimony by electrothermal atomic absorption is described. It was found that the negative influence of the hydrofluoric acid, used for the digestion could not be eliminated by using stabilized temperature platform furnace (STPF) alone. Due to the high dissociation energy (D(0)=506kJmol(-1)) of indium fluoride, it is difficult to dissociate in the gas phase and hence is lost. In presence of HF (used for the dissolution of antimony), the universal Pd-Mg modifier does not work satisfactorily. Additionally, rising corrosion and reduced tube lifetime were observed when the acid digested (HF-HNO(3)) antimony solution was injected in to the platform. Improvement in platform life and elimination of interferences were achieved by the addition of boric acid as a chemical modifier together with ruthenium coating of the platform. Corrosive changes of the transversely heated graphite atomizer (THGA) platform surface were examined by scanning electron microscopy. The standard addition method was applied. A characteristic mass of 36pg was obtained. The detection limit of the proposed method is around 0.04mugg(-1). The developed method was applied to the determination of indium in real samples. The data obtained by this method were in good agreement with those obtained by ICP-MS.